苏州玻璃增强PBT/PC IQ507!2022已更新(今日/新闻)
点击图片查看原图
|
|
产品: |
苏州玻璃增强PBT/PC IQ507 |
品牌: |
SABIC |
型号: |
IQ507 |
规格: |
PC/ABS |
单价: |
1.00元/KG |
最小起订量: |
25 KG |
供货总量: |
5000 KG |
发货期限: |
自买家付款之日起 3 天内发货 |
有效期至: |
长期有效 |
最后更新: |
2016-04-01 14:08 |
|
|
|
苏州玻璃增强PBT/PC IQ507!2022已更新(今日/新闻)
型号:PBT/PC IQ507
性能:通用级,PBT/PC,30%玻璃增强。
VALOX™ Resin IQ507
|
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characteristics, along with reduced warpage characteristics.
|
|
TYPICAL PROPERTIES (1) |
MECHANICAL
|
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 5 mm/min
|
1070
|
kgf/cm²
|
ASTM D 638
|
Tensile Stress, brk, Type I, 5 mm/min
|
1070
|
kgf/cm²
|
ASTM D 638
|
Tensile Stress, brk, Type I, 10 mm/min
|
1340
|
kgf/cm²
|
SABIC - Japan Method
|
Tensile Strain, yld, Type I, 5 mm/min
|
1
|
%
|
ASTM D 638
|
Tensile Strain, brk, Type I, 5 mm/min
|
1
|
%
|
ASTM D 638
|
Tensile Strain, brk, Type I, 10 mm/min
|
7
|
%
|
SABIC - Japan Method
|
Tensile Modulus, 5 mm/min
|
130500
|
kgf/cm²
|
ASTM D 638
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1990
|
kgf/cm²
|
ASTM D 790
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
92400
|
kgf/cm²
|
ASTM D 790
|
Hardness, Rockwell R
|
119
|
-
|
ASTM D 785
|
Tensile Stress, yield, 5 mm/min
|
96
|
MPa
|
ISO 527
|
Tensile Stress, break, 5 mm/min
|
96
|
MPa
|
ISO 527
|
Tensile Strain, yield, 5 mm/min
|
1
|
%
|
ISO 527
|
Tensile Strain, break, 5 mm/min
|
1
|
%
|
ISO 527
|
Tensile Modulus, 1 mm/min
|
10200
|
MPa
|
ISO 527
|
Flexural Stress, yield, 2 mm/min
|
187
|
MPa
|
ISO 178
|
Flexural Modulus, 2 mm/min
|
8910
|
MPa
|
ISO 178
|
IMPACT
|
Value |
Unit |
Standard |
Izod Impact, unnotched, 23°C
|
60
|
cm-kgf/cm
|
ASTM D 4812
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
Izod Impact, notched, -30°C
|
7
|
cm-kgf/cm
|
ASTM D 256
|
Instrumented Impact Total Energy, 23°C
|
71
|
cm-kgf
|
ASTM D 3763
|
Izod Impact, notched 80*10*4 +23°C
|
8
|
kJ/m²
|
ISO 180/1A
|
Izod Impact, notched 80*10*4 -30°C
|
7
|
kJ/m²
|
ISO 180/1A
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
21
|
kJ/m²
|
ISO 179/1eA
|
THERMAL
|
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50
|
192
|
°C
|
ASTM D 1525
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
182
|
°C
|
ASTM D 648
|
CTE, -40°C to 40°C, flow
|
2.1E-05
|
1/°C
|
ASTM E 831
|
CTE, -40°C to 40°C, xflow
|
8.1E-05
|
1/°C
|
ASTM E 831
|
CTE, -40°C to 40°C, flow
|
2.1E-05
|
1/°C
|
ISO 11359-2
|
CTE, -40°C to 40°C, xflow
|
8.1E-05
|
1/°C
|
ISO 11359-2
|
Vicat Softening Temp, Rate B/50
|
192
|
°C
|
ISO 306
|
Vicat Softening Temp, Rate B/120
|
190
|
°C
|
ISO 306
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
212
|
°C
|
ISO 75/Bf
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
186
|
°C
|
ISO 75/Af
|
PHYSICAL
|
Value |
Unit |
Standard |
Specific Gravity
|
1.51
|
-
|
ASTM D 792
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.1 - 0.4
|
%
|
SABIC Method
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.4 - 0.8
|
%
|
SABIC Method
|
Melt Flow Rate, 250°C/5.0 kgf
|
50
|
g/10 min
|
ASTM D 1238
|
Density
|
1.51
|
g/cm³
|
ISO 1183
|
Water Absorption, (23°C/sat)
|
0.1
|
%
|
ISO 62
|
Moisture Absorption (23°C / 50% RH)
|
0.08
|
%
|
ISO 62
|
Melt Volume Rate, MVR at 220°C/5.0 kg
|
43
|
cm³/10 min
|
ISO 1133
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
38
|
cm³/10 min
|
ISO 1133
|
Source GMD, last updated:2007/11/01
|
Parameter |
Injection Molding
|
Value |
Unit |
Drying Temperature
|
120
|
°C
|
Drying Time
|
3 - 4
|
hrs
|
Drying Time (Cumulative)
|
12
|
hrs
|
Maximum Moisture Content
|
0.02
|
%
|
Melt Temperature
|
250 - 265
|
°C
|
Nozzle Temperature
|
245 - 260
|
°C
|
Front - Zone 3 Temperature
|
250 - 265
|
°C
|
Middle - Zone 2 Temperature
|
245 - 260
|
°C
|
Rear - Zone 1 Temperature
|
240 - 255
|
°C
|
Mold Temperature
|
65 - 90
|
°C
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
Screw Speed
|
50 - 80
|
rpm
|
Shot to Cylinder Size
|
40 - 80
|
%
|
Vent Depth
|
0.025 - 0.038
|
mm
|
公司其他供应信息
| 苏州LCP A150F 通用级
| 苏州日本东丽LCP L204G35R
| 苏州LCP Zenite 5145L
| 苏州Sumikasuper LCP E4008
| 苏州阻燃ABS AF360C
| 苏州通用级PBT/PC 9X02841
| 苏州玻璃纤维PBT/PC 9X07430
| 苏州冲击改性PBT/PC 3706
| 苏州耐热性能PBT/PC 508R
| 苏州通用级PBT/PC 553U
|