您当前的位置： 首页 » 供应产品 » 苏州玻璃纤维PBT/PC 9X07430 苏州玻璃纤维PBT/PC 9X07430!2022已更新(今日/新闻)
 点击图片查看原图 |
|
| 产品： |
苏州玻璃纤维PBT/PC 9X07430 |
| 品牌： |
SABIC |
| 型号： |
9X07430 |
| 规格： |
PBT/PC |
| 单价： |
1.00元/KG |
| 最小起订量： |
25 KG |
| 供货总量： |
5000 KG |
| 发货期限： |
自买家付款之日起 3 天内发货 |
| 有效期至： |
长期有效 |
| 最后更新： |
2016-03-31 00:11 |
| |
 |
|
苏州玻璃纤维PBT/PC 9X07430!2022已更新(今日/新闻)
型号：PBT/PC 9X07430
性能：通用级，PBT/PC，玻璃纤维。
|
LNP™THERMOCOMP™ Compound 9X07430
|
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
| Also known as:LNP™Thermocomp™Compound 9X07430 |
| Product reorder name:9X07430 |
| |
|
PBT+PC Alloy, Glass and Mineral Filled, Opaque, Weatherable
|
| |
| TYPICAL PROPERTIES (1) |
|
MECHANICAL
|
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 5 mm/min
|
580
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
520
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
2.9
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
4.8
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
33600
|
kgf/cm²
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1000
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
32000
|
kgf/cm²
|
ASTM D 790
|
|
Tensile Stress, yield, 5 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
56
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
3.1
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
4.9
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
3160
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
97
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
3020
|
MPa
|
ISO 178
|
|
IMPACT
|
Value |
Unit |
Standard |
|
Izod Impact, unnotched, 23°C
|
72
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Energy @ peak, 23°C
|
91
|
cm-kgf
|
ASTM D 3763
|
|
Instrumented Impact Energy @ peak, -30
|
30
|
cm-kgf
|
ASTM D 3763
|
|
Multiaxial Impact
|
71
|
cm-kgf
|
ISO 6603
|
|
Instrumented Impact Total Energy, 23°C
|
142
|
cm-kgf
|
ASTM D 3763
|
|
Instrumented Impact Total Energy, -30°C
|
71
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
47
|
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
8
|
kJ/m²
|
ISO 180/1A
|
|
THERMAL
|
Value |
Unit |
Standard |
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
102
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
5.7E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
8.3E-05
|
1/°C
|
ASTM E 831
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
105
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value |
Unit |
Standard |
|
Density
|
1.31
|
g/cm³
|
ASTM D 792
|
|
Moisture Absorption, 50% RH, 24 hrs
|
0.11
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow (5)
|
0.51
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow (5)
|
0.59
|
%
|
SABIC Method
|
|
Mold Shrinkage, flow, 24 hrs (5)
|
0.5 - 0.51
|
%
|
ASTM D 955
|
|
Mold Shrinkage, xflow, 24 hrs (5)
|
0.58 - 0.59
|
%
|
ASTM D 955
|
|
Density
|
1.31
|
g/cm³
|
ISO 1183
|
|
Moisture Absorption (23°C / 50% RH)
|
0.16
|
%
|
ISO 62
|
|
Source GMD, last updated:2011/01/20
|
| Parameter |
|
Injection Molding
|
Value |
Unit |
|
Drying Temperature
|
80 - 110
|
°C
|
|
Drying Time
|
4 - 6
|
hrs
|
|
Drying Time (Cumulative)
|
24
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
260 - 280
|
°C
|
|
Nozzle Temperature
|
260 - 280
|
°C
|
|
Front - Zone 3 Temperature
|
260 - 280
|
°C
|
|
Middle - Zone 2 Temperature
|
255 - 275
|
°C
|
|
Rear - Zone 1 Temperature
|
245 - 270
|
°C
|
|
Mold Temperature
|
80 - 110
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
| 苏州LCP A150F 通用级
| 苏州日本东丽LCP L204G35R
| 苏州LCP Zenite 5145L
| 苏州Sumikasuper LCP E4008
| 苏州阻燃ABS AF360C
| 苏州通用级PBT/PC 9X02841
| 苏州玻璃纤维PBT/PC 9X07430
| 苏州冲击改性PBT/PC 3706
| 苏州耐热性能PBT/PC 508R
| 苏州通用级PBT/PC 553U
|