您当前的位置: 首页 » 供应产品 » 苏州通用级PBT/PC 9X02841
苏州通用级PBT/PC 9X02841!2022已更新(今日/新闻)
点击图片查看原图
|
|
产品: |
苏州通用级PBT/PC 9X02841 |
品牌: |
SABIC |
型号: |
9X02841 |
规格: |
PBT/PC |
单价: |
1.00元/KG |
最小起订量: |
25 KG |
供货总量: |
5000 KG |
发货期限: |
自买家付款之日起 3 天内发货 |
有效期至: |
长期有效 |
最后更新: |
2016-03-31 00:11 |
|
|
|
苏州通用级PBT/PC 9X02841!2022已更新(今日/新闻)
型号:PBT/PC 9X02841
性能:通用级,PBT/PC,专有填料(s)。
LNP™THERMOCOMP™ Compound 9X02841
|
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
Also known as:LNP™Thermocomp™Compound PDX-02841 |
Product reorder name:9X02841 |
|
LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers.
|
|
TYPICAL PROPERTIES (1) |
MECHANICAL
|
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 5 mm/min
|
840
|
kgf/cm²
|
ASTM D 638
|
Tensile Stress, brk, Type I, 5 mm/min
|
840
|
kgf/cm²
|
ASTM D 638
|
Tensile Strain, yld, Type I, 5 mm/min
|
2.7
|
%
|
ASTM D 638
|
Tensile Strain, brk, Type I, 5 mm/min
|
2.7
|
%
|
ASTM D 638
|
Tensile Modulus, 50 mm/min
|
52200
|
kgf/cm²
|
ASTM D 638
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
1290
|
kgf/cm²
|
ASTM D 790
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1250
|
kgf/cm²
|
ASTM D 790
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
46900
|
kgf/cm²
|
ASTM D 790
|
Tensile Stress, yield, 5 mm/min
|
80
|
MPa
|
ISO 527
|
Tensile Stress, break, 5 mm/min
|
80
|
MPa
|
ISO 527
|
Tensile Strain, yield, 5 mm/min
|
2.6
|
%
|
ISO 527
|
Tensile Strain, break, 5 mm/min
|
2.6
|
%
|
ISO 527
|
Tensile Modulus, 1 mm/min
|
4880
|
MPa
|
ISO 527
|
Flexural Stress
|
115
|
MPa
|
ISO 178
|
Flexural Modulus, 2 mm/min
|
4480
|
MPa
|
ISO 178
|
IMPACT
|
Value |
Unit |
Standard |
Izod Impact, unnotched, 23°C
|
53
|
cm-kgf/cm
|
ASTM D 4812
|
Izod Impact, notched, 23°C
|
7
|
cm-kgf/cm
|
ASTM D 256
|
Multiaxial Impact
|
45
|
cm-kgf
|
ISO 6603
|
Instrumented Impact Total Energy, 23°C
|
171
|
cm-kgf
|
ASTM D 3763
|
Izod Impact, unnotched 80*10*4 +23°C
|
31
|
kJ/m²
|
ISO 180/1U
|
Izod Impact, notched 80*10*4 +23°C
|
7
|
kJ/m²
|
ISO 180/1A
|
THERMAL
|
Value |
Unit |
Standard |
HDT, 0.45 MPa, 3.2 mm, unannealed
|
141
|
°C
|
ASTM D 648
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
115
|
°C
|
ASTM D 648
|
CTE, -30°C to 30°C, flow
|
4.1E-05
|
1/°C
|
ASTM D 696
|
CTE, -30°C to 30°C, xflow
|
6.3E-05
|
1/°C
|
ASTM D 696
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
140
|
°C
|
ISO 75/Bf
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
115
|
°C
|
ISO 75/Af
|
PHYSICAL
|
Value |
Unit |
Standard |
Density
|
1.33
|
g/cm³
|
ASTM D 792
|
Moisture Absorption, 50% RH, 24 hrs
|
0.09
|
%
|
ASTM D 570
|
Mold Shrinkage, flow, 24 hrs (5)
|
0.4 - 0.6
|
%
|
ASTM D 955
|
Mold Shrinkage, xflow, 24 hrs (5)
|
0.6 - 0.8
|
%
|
ASTM D 955
|
Density
|
1.33
|
g/cm³
|
ISO 1183
|
Moisture Absorption (23°C / 50% RH)
|
0.14
|
%
|
ISO 62
|
Source GMD, last updated:2008/11/21
|
Parameter |
Injection Molding
|
Value |
Unit |
Drying Temperature
|
120
|
°C
|
Drying Time
|
4
|
hrs
|
Maximum Moisture Content
|
0.05
|
%
|
Melt Temperature
|
240 - 265
|
°C
|
Front - Zone 3 Temperature
|
260 - 270
|
°C
|
Middle - Zone 2 Temperature
|
245 - 255
|
°C
|
Rear - Zone 1 Temperature
|
220 - 230
|
°C
|
Mold Temperature
|
80 - 100
|
°C
|
Back Pressure
|
0.2 - 0.3
|
MPa
|
Screw Speed
|
30 - 60
|
rpm
|
公司其他供应信息
| 苏州LCP A150F 通用级
| 苏州日本东丽LCP L204G35R
| 苏州LCP Zenite 5145L
| 苏州Sumikasuper LCP E4008
| 苏州阻燃ABS AF360C
| 苏州通用级PBT/PC 9X02841
| 苏州玻璃纤维PBT/PC 9X07430
| 苏州冲击改性PBT/PC 3706
| 苏州耐热性能PBT/PC 508R
| 苏州通用级PBT/PC 553U
|